Experimental analysis reveals wear behavior of WE54 alloy at varying heat treatments and temperatures, indicating significant effects on tribological properties.
This study examines the high-temperature tribological behavior of WE54 Mg alloy under various conditions: as-cast, solution-treated (T4), age-hardened (T6), and secondary aged (S.A). Wear tests were performed using a pin-on-disc setup, applying a normal load of 10 N, with a sliding velocity of 1 m/s, a sliding distance of 1000 m, and temperatures from 25 °C to 150 °C. Responses such as the coefficient of friction and volumetric wear rate were recorded. The results indicate that heat treatment significantly influences the wear behavior of the WE54 alloy. The lowest volumetric wear rate (8.16 ± 1.47 mm3) and wear coefficient (0.112 ± 0.02) occurred in the as-cast sample at 100 °C, while the highest volumetric wear rate (14.68 ± 1.59 mm3) and wear coefficient (0.171 ± 0.02) were found in the S.A. sample at 150 °C. Surface characterization of worn samples was conducted using field emission scanning electron microscopy (FESEM) and X-ray diffraction (XRD). The wear mechanisms identified include abrasive wear, oxidative wear, and delamination across all conditions, regardless of temperature. The elevated volumetric wear rate at 150 °C, irrespective of the sample condition, is attributed to oxidation and thermal softening of the material.
No takes yet. Share an insight, caveat, or question.
Saravanan et al. (2025) studied this question.