K-TIG welding improves mechanical strength and corrosion resistance in 2205 and 316L stainless steel joints, suggesting enhanced industrial applications.
Stainless steel welding plays a critical role in industrial manufacturing due to its superior corrosion resistance and structural reliability. The keyhole tungsten inert gas (K-TIG) welding, renowned for its high efficiency, high precision, and cost-effectiveness, demonstrates particular advantages in medium-to-thick plate joining. In order to synergistically leverage the properties of 2205 duplex stainless steel (DSS) and 316L austenitic stainless steel (ASS), we have implemented K-TIG welding with a single variable under control: a constant current and voltage travelling speeds spanning 280–360 mm/min. Defect-free dissimilar joints were consistently achieved within the 280–320 mm/min speed window. The effects of welding speed on microstructural characteristics, mechanical properties, and corrosion behavior of the weld seams were systematically investigated. The percentage of austenite in the weld zone decreases from 84.7% to 59.9% as the welding speed increases. At a welding speed of 280 mm/min, the microstructural features in the regions near the weld seam and fusion zone were investigated. All obtained joints exhibited excellent tensile properties, with their tensile strengths surpassing those of the 316L base metal. The optimal impact toughness of 142 J was achieved at a welding speed of 320 mm/min. The obtained joints exceeded the hardness of TIG joints by 19%. Notably, the grain refinement in the weld zone not only enhanced the hardness of the welded joint but also improved its corrosion resistance. This study provides valuable process references in dissimilar stainless steel K-TIG welding applications.
No takes yet. Share an insight, caveat, or question.
Cui et al. (2025) studied this question.