Thermodynamic Modeling of Microstructural Design of Lightweight Ferritic Steels

Ferritic lightweight steels are an emerging class of low-density steels (LDSs) with promising mechanical properties. The study aimed to develop two ferritic lightweight steels with different Mn concentrations. Al was incorporated to achieve the lightweighting effect due to its relatively low atomic mass of substitutional solutions. The C concentration was kept at a minimum level to avoid the precipitation of carbides and the Mn addition was intended to increase solid solution strengthening. Thermodynamic calculations (Thermo-Calc) were employed to design the composition, analyze the phase constituents, and predict the phase transformation behavior. Microstructural investigation and hardness tests were conducted to experimentally verify the calculations. Both produced alloys exhibited a fully ferritic microstructure. Compared to industrially produced DP980 steel, a density reduction of about 7.2% and 8.3% was attained for the Fe-0.04C-5.5Al-1.6Mn-0.075Nb and Fe-0.04C-5.6Al-5.5Mn-0.08Nb steels, respectively. The steel with the higher Mn content showed increased hardness attributed to its solution strengthening effect. An increase in the hardness values was also measured with the progress in hot-rolling thickness reductions for both alloys. The alloying elements influenced the microstructural characteristics, phase transformation behavior, density, and hardness of the newly designed lightweight steels.